Position:Home > Product > aluminum coil >

3003 aluminum coil

[field:text/]
  • Product: 3003 h14 aluminum coil strips suppli
  • Loading Port: Tianjin/Qingdao, China
  • Sample: A4 Sized
  • Payment Terms: L/C,D/P,T/T
  • Delivery time: Within 15-30 Days
  • Application: inland marine equipment construction and decorationconductive materialsroad signshardware

Get Latest Price

Product Detail

3003 aluminum coil is the most widely used aluminum alloy. It is made up of aluminum, copper, iron, manganese, silicon and zinc. It is commonly used because it has great resistance to corrosion and is moderately strong. The 3003 aluminum coil is 20% stronger than 1100 grade alloys because it is fused with manganese.
 

Because it’s not heat treatable, it has to be strengthened using cold working alone.
The most common applications for the 3003 aluminum coil are for fuel tanks, sheet metal work and other types of projects that need a metal that is stronger than the 1100 series aluminum. In some cases, it is used for cooking utensils, refrigerator panels, gas lines, storage tanks, garage doors, builder’s hardware and awning slats.

Material Tensile properties Brinell hardness
HBS10/500
Fatigue strength
/Mpa
∂b/Mpa ∂0.2/Mpa ∂/%
3003-O 110 40 30 28 50
3003-H12 130 125 10 35 55
3003-H14 150 145 8 40 60
3003-H16 175 170 5 47 70
3003-H18 200 185 4 55 70
 
 
The machinability of the 3003 Aluminum is considered good for being an aluminum alloy. It is readily machined for the different applications. It can either be formed using conventional hot working or cold working. It’s also possible to use conventional welding methods to shape 3003 aluminum. It is sometimes welded to other aluminum alloys, like 6061, 5052 and 6062, which should have an AL 4043 filler rod.
 
AL 3003 isn’t heat treatable, but it can be forged with heat that’s between 500 and 950 degrees Fahrenheit. When using heat in this range, the aluminum can be hot worked easily. However, it is readily cold worked, which can be done using conventional methods. When annealing the alloy during or after using cold working techniques, it should be performed at 775 degrees Fahrenheit. This will give it enough time to thoroughly heat before being air cooled. The only way to make this alloy hard is with the use of cold working. It can also be deep drawn, spun or brazed.

Contact

Henan Mingtai Aluminum Inductrial Co.,Ltd

Marketing hotline: +86-15237181905

Email: sales01@mingtai-al.com

Company address: No.6, Changchun Road, High-tech

Industrial Development Zone, Zhengzhou City